Effect of water/binder ratio and temperature on the hydration heat and properties of ternary blended cement containing slag and iron tailing powder

Journal of Thermal Analysis and Calorimetry - The effects of water/binder ratio and temperature on hydration heat and properties of ternary blended cement containing slag and iron tailing powder...     

动、静裂纹作用偏置效应的动焦散冲击实验

为了研究冲击荷载作用下脆性材料中运动裂纹与静止裂纹的相互作用，选取动态载荷下断裂行为与岩石材料类似且本身光学特性较好的有机玻璃（PMMA）作为实验材料，试件尺寸为220 mm×50 mm×5 mm，采用激光切割制作长度5 mm的预制裂纹和长度10 mm的静止裂纹，预制裂纹位于试件的底部边缘中心，静止裂纹的中心位于试件水平轴线。将静止裂纹偏置距离作为单一变量，采用数字激光动态焦散实验系统对含不同缺陷的PMMA进行三点弯曲实验，并结合几何分形理论研究不同偏置距离下运动裂纹的分形规律。实验结果表明:存在预制裂纹与静止裂纹的临界偏置距离（6 mm），该条件下裂纹轨迹对应的分形维数值最大，裂纹轨迹的规则程度最低，裂纹破坏形态最复杂。当预制裂纹与静止裂纹的偏置距离在0～6 mm时，裂纹Ⅰ起裂后垂直向上扩展一段距离，与静止裂纹交汇，并停滞一段时间后发生二次起裂，直至贯穿试件，偏置距离和交汇点竖向坐标值呈近似线性函数关系。偏置距离的存在不会影响裂纹Ⅰ的起裂时间和应力强度因子，但会显著减小裂纹Ⅱ的动态应力强度因子，且停滞时长随偏置距离的增大而逐渐缩短。当偏置距离大于临界偏置距离时，运动裂纹不再与静止裂纹交汇而是呈拱状向试件上边缘扩展直至贯穿，裂纹的起偏时间、起偏位置也会出现明显的滞后现象。     

Hydration,mechanical properties and durability of high-strength concrete under different curing conditions

The properties of high-strength concrete under standard curing condition (20 °C, 95% RH), high-temperature curing condition (50 °C) and temperature match curing condition were comparatively investigated. The cumulative hydration heat of composite binder containing fly ash and silica fume is lower than that of composite binder containing the same amount of slag. Addition of fly ash and silica fume clearly reduces the adiabatic temperature rise of concrete, but adding slag leads to higher adiabatic temperature rise than Portland cement concrete. High-temperature curing condition and temperature match curing condition lead to the sustainable increase in compressive strength of concrete containing mineral admixture, but they hinder the later-age strength development of Portland cement concrete. For cement–slag paste and cement–fly ash–silica fume paste, the non-evaporable water contents increase significantly and the pore structures are much finer under high-temperature curing condition and temperature match curing condition, which negatively affect the pore structure of Portland cement paste. The differences in properties of concrete among three curing conditions become smaller with time. The properties obtained under standard curing condition can approximately reflect the long-term properties of high-strength concrete in the real structure. The concrete prepared with cement–fly ash–silica fume composite binder has the highest compressive strength, finest pore structure and best resistance to chloride permeability under any curing condition. This composite binder is very suitable to prepare the high-strength concrete with large volume.     

基于DIC技术的爆炸应力波过异质界面应变场演化规律实验研究

采用氯仿粘结聚碳酸酯（polycarbonate, PC）板和聚甲基丙烯酸甲酯（polymethylmethacrylate, PMMA）板模拟含异质界面模型;在PC介质中布置柱状炮孔并与界面呈一定角度,根据炮孔端部与界面相对位置,分别于柱状炮孔两个端部设置起爆点,起爆点远离界面端部时定义为孔口起爆,靠近界面端部时定义为孔底起爆;借助数字图像相关实验系统,研究爆炸应力波通过异质界面后PMMA介质应变场演化过程及炮孔底部区域拉、压应变变化规律。实验结果表明,异质界面改变了爆炸应力波过界面后的传播形态。孔口起爆时,异质界面受爆破荷载作用后易形成应力集中区,界面处产生开裂,横向拉伸波作用是造成异质界面开裂的主要原因。起爆方式对过界面后介质PMMA的横/纵向拉、压应变场作用贡献不同,主要体现在应变场强度、拉/压应变场位置分布2个方面。在炮孔底部区域,起爆方式对应变场时程特性的影响主要体现在作用时效长短和应变强度2个方面。孔口起爆时,横/纵向应变体现出短时效、高强度的变化特征。就应变强度而言,起爆方式对横向压应变的影响显著强于其对纵向拉应变的影响。对空间分布特性影响主要体现在衰减程度,起爆方式对纵向应变衰减程度影响较大。无论采用何种起爆方式,爆炸应变场在PC介质中衰减速度较快,进入PMMA介质后衰减速度显著降低。